Composite substrate for electro-optic element and method for manufacturing the same

ABSTRACT

A composite substrate for an electro-optic element is disclosed. The composite substrate includes: an electro-optic crystal substrate having an electro-optic effect; a support substrate bonded to the electro-optic crystal substrate at least via an amorphous layer; and a low-refractive-index layer located between the electro-optic crystal substrate and the amorphous layer and having a lower refractive index than the electro-optical crystal substrate. The amorphous layer is constituted of one or more elements that constitute a layer or a substrate contacting the amorphous layer from one side and one or more elements that constitute a layer or a substrate contacting the amorphous layer from another side.

CROSS-REFERENCE TO RELATED APPLICATION

This is a continuation of PCT/JP2018/019657 filed on May 22, 2018, the entire contents of which are hereby incorporated by reference.

TECHNICAL FIELD

The art disclosed herein relates to a composite substrate for an electro-optic element (such as an optical modulator) that uses an electro-optic effect.

BACKGROUND

An electro-optic element such as an optical modulator is known. The electro-optic element is configured to use an electro-optic effect to convert an electric signal to an optical signal. Electro-optic elements are employed in radio-over-fiber technologies, for example, and development thereof is in progress to realize fast and large-capacity communication.

Japanese Patent Application Publication No. 2010-85789 describes an optical modulator. This optical modulator is configured by using a composite substrate. The composite substrate includes an electro-optic crystal substrate having an electro-optic effect and a support substrate bonded to the electro-optic crystal substrate.

SUMMARY

In a conventional composite substrate, an electro-optic crystal substrate and a support substrate are bonded by adhesive. With such a configuration, the adhesive may be degraded over time, as a result of which a separation may occur in the composite substrate, and damages such as a crack may occur in the electro-optic crystal substrate due to this separation. To avoid such issues, the electro-optic crystal substrate may directly be bonded to the support substrate without using the adhesive. However, when the electro-optic crystal substrate and the support substrate are directly bonded, an amorphous layer constituted of elements of the electro-optic crystal substrate and elements of the support substrate is formed between the electro-optic crystal substrate and the support substrate. This amorphous layer does not have crystallinity, its optical property differs from those of the substrates on its both sides, and an interface between the electro-optic crystal substrate and the amorphous layer is not flat. Such a non-flat interface has a risk of diffusing (such as diffused reflection or leakage) and absorbing light transmitted through the electro-optic crystal substrate.

Thus, the disclosure herein provides a composite substrate which may avoid or reduce aforementioned issues, and a method of manufacturing the same.

The disclosure herein discloses a composite substrate for an electro-optic element. This composite substrate comprises: an electro-optic crystal substrate having an electro-optic effect; a support substrate bonded to the electro-optic crystal substrate at least via an amorphous layer; and a low-refractive-index layer located between the electro-optic crystal substrate and the amorphous layer and having a lower refractive index than the electro-optical crystal substrate. The amorphous layer is constituted of one or more elements that constitute a layer or a substrate contacting the amorphous layer from one side and one or more elements that constitute a layer or a substrate contacting the amorphous layer from another side.

The aforementioned composite substrate can be manufactured by a manufacturing method as follows. This manufacturing method comprises: depositing at least one layer comprising a low-refractive-index layer on an electro-optic crystal substrate having an electro-optic effect, the low-refractive-index layer having a lower refractive index than the electro-optic crystal substrate; and directly bonding the electro-optic crystal substrate on which the at least one layer is deposited to a surface of a support substrate. The wording “directly bonding” referred herein means bonding in which atoms diffuse between two members that are bonded and a covalent bond is formed between those atoms. Prior to the direct bonding, at least one layer may be deposited on the surface of the support substrate.

According to the aforementioned manufacturing method, the composite substrate in which the support substrate is bonded to the electro-optic crystal substrate can be manufactured without using adhesive. The amorphous layer resulting from the direct bonding is formed in the manufactured composite substrate, however, the low-refractive-index layer is interposed between the amorphous layer and the electro-optic crystal substrate, as a result of which the amorphous layer is not in contact with the electro-optic crystal substrate. As such, light transmitted through the electro-optic crystal substrate is not diffused nor absorbed by the amorphous layer or at a non-flat interface between the amorphous layer and the electro-optic crystal substrate. In addition, the low-refractive-index layer that is in contact with the electro-optic crystal substrate has the lower refractive index than the electro-optic crystal substrate, thus, similar to a clad in an optical fiber, the low-refractive-index layer can suppress leakage of the light transmitted through the electro-optic crystal substrate. By using this composite substrate, an electro-optic element with high performance and durability can be manufactured.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a perspective view schematically showing a composite substrate 10 of a first embodiment.

FIG. 2 schematically shows a cross-sectional structure of the composite substrate 10 of the first embodiment.

FIG. 3 shows a step of a method of manufacturing the composite substrate 10 of the first embodiment.

FIG. 4 shows a step of the method of manufacturing the composite substrate 10 of the first embodiment.

FIG. 5 shows a step of the method of manufacturing the composite substrate 10 of the first embodiment.

FIG. 6 shows a variant of the composite substrate 10, and electrodes 32, 34 configured to generate an electric field in an electro-optic crystal substrate 12 and an optical waveguide region 36 arranged in the electro-optic crystal substrate 12 are added.

FIG. 7 shows a variant of the composite substrate 10, and a ridge portion 13 is arranged on a top surface 12 a of the electro-optic crystal substrate 12.

FIG. 8 shows a variant of the composite substrate 10, and as compared to the variant shown in FIG. 7, a first electrode 42 and a second electrode 44 are added. In this variant, a c-axis of the electro-optic crystal substrate 12 is parallel to the electro-optic crystal substrate 12.

FIG. 9 shows a variant of the composite substrate 10, and as compared to the variant shown in FIG. 7, a first electrode 52 and a second electrode 54 are added. In this variant, the c-axis of the electro-optic crystal substrate 12 is perpendicular to the electro-optic crystal substrate 12.

FIG. 10 schematically shows a cross-sectional structure of a composite substrate 10 a of a second embodiment.

FIG. 11 is a diagram explaining a method of manufacturing the composite substrate 10 a of the second embodiment.

FIG. 12 schematically shows a cross-sectional structure of a composite substrate 10 b of a third embodiment.

FIG. 13 shows a diagram explaining a method of manufacturing the composite substrate 10 b of the third embodiment.

FIG. 14 schematically shows a cross-sectional structure of a composite substrate 10 c of a fourth embodiment.

FIG. 15 shows a diagram explaining a method of manufacturing the composite substrate 10 c of the fourth embodiment.

FIG. 16 schematically shows a cross-sectional structure of a composite substrate 10 d of a fifth embodiment.

FIG. 17 shows a diagram explaining a method of manufacturing the composite substrate 10 d of the fifth embodiment.

FIG. 18 schematically shows a cross-sectional structure of a composite substrate 10 e of a sixth embodiment.

FIG. 19 shows a diagram explaining a method of manufacturing the composite substrate 10 e of the sixth embodiment.

FIG. 20 schematically shows a cross-sectional structure of a composite substrate 10 f of a seventh embodiment.

FIG. 21 shows a diagram explaining a method of manufacturing the composite substrate 10 f of the seventh embodiment.

FIG. 22 schematically shows a cross-sectional structure of a composite substrate 10 g of an eighth embodiment.

FIG. 23 shows a diagram explaining a method of manufacturing the composite substrate 10 g of the eighth embodiment.

FIG. 24 schematically shows a cross-sectional structure of a composite substrate 10 h of a ninth embodiment.

FIG. 25 shows a diagram explaining a method of manufacturing the composite substrate 10 h of the ninth embodiment.

FIG. 26 schematically shows a cross-sectional structure of a composite substrate 10 i of a tenth embodiment.

FIG. 27 shows a diagram explaining a method of manufacturing the composite substrate 10 i of the tenth embodiment.

FIG. 28 schematically shows a cross-sectional structure of a composite substrate 10 j of an eleventh embodiment.

FIG. 29 shows a diagram explaining a method of manufacturing the composite substrate 10 j of the eleventh embodiment.

DETAILED DESCRIPTION

In an embodiment of the disclosure herein, an electro-optic crystal substrate may be a substrate of lithium niobate (LiNbO₃: LN), lithium tantalate (LiTaO₃: LT), potassium titanyl phosphate (KTiOPO₄: KTP), potassium lithium niobate (K_(x)Li_((1-x))NbO₂: KLN), potassium niobate (KNbO₃: KN), potassium tantalate niobate (KNb_(x)Ta_((1-x))O₃: KTN), or a solid solution of lithium niobate and lithium tantalite.

In an embodiment of the disclosure herein, the low-refractive-index layer may be constituted of at least one selected from a group consisting of silicon oxide (SiO₂), tantalum oxide (Ta₂O₅), aluminum oxide (Al₂O₃), magnesium fluoride (MgF₂), and calcium fluoride (CaF₂).

In an embodiment of the disclosure herein, the support substrate may be a substrate of silicon (Si), glass, sialon (Si₃N₄—Al₂O₃), mullite (3Al₂O₃.2SiO₂,2Al₂O₃.SiO₂), aluminum nitride (AlN), silicon nitride (Si₃N₄), magnesium oxide (MgO), sapphire, quartz, crystal, gallium nitride (GaN), silicon carbide (SiC), or gallium oxide (Ga₂O₃).

In an embodiment of the disclosure herein, the layer or substrate contacting the amorphous layer from the one side may be the low-refractive-index layer. Such a composite substrate can be manufactured by directly bonding the electro-optic crystal substrate on which the low-refractive-index layer is deposited to the support substrate. In this configuration, at least one layer may be deposited on the surface of the support substrate in advance.

In an embodiment of the art disclosed herein, the composite substrate may further comprise a first conductive layer located between the low-refractive-index layer and the amorphous layer. In this case, the layer or substrate contacting the amorphous layer from the one side may be the first conductive layer. Such a composite substrate can be manufactured by directly bonding the electro-optic crystal substrate on which the first conductive layer is deposited on the low-refractive-index layer to the support substrate. In this configuration, at least one layer may be deposited on the surface of the support substrate in advance. In the electro-optic element manufactured from the composite substrate, the first conductive layer may be used as an electrode for applying an electric signal (that is, an electric field) to the electro-optic crystal substrate. Alternatively, the first conductive layer may be used as a shield for suppressing the electric field from leaking from the electro-optic element.

The first conductive layer may comprise a layer of gold (Au), silver (Ag), copper (Cu), aluminum (Al), platinum (Pt), or an alloy containing at least two of the aforementioned elements. The first conductive layer may have a single layer structure or a multiple layer structure.

A surface layer of the first conductive layer contacting the amorphous layer may be constituted of platinum. Platinum is a material suitable for direct bonding. Due to this, when the surface layer of the first conductive layer is constituted of platinum, the electro-optic crystal substrate on which the first conductive layer is deposited can suitably be bonded directly to the support substrate.

In the aforementioned embodiment, the composite substrate may further comprise a first bonding layer located between the low-refractive-index layer and the amorphous layer. In this case, the layer or substrate contacting the amorphous layer from the one side may be the first bonding layer. A material constituting the first bonding layer may be, but not particularly limited to, a material suitable for direct bonding, such as tantalum oxide (Ta₂O₅), niobium oxide (Nb₂O₅), silicon (Si), aluminum oxide (Al₂O₃), and titanium oxide (TiO₂), for example.

In the aforementioned embodiment, the composite substrate may further comprise a first conductive layer located between the low-refractive-index layer and the first bonding layer. In the electro-optic element manufactured from the composite substrate, the first conductive layer may be used as an electrode for applying an electric signal (that is, an electric field) to the electro-optic crystal substrate. Alternatively, the first conductive layer may be used as a shield for suppressing the electric field from leaking from the electro-optic element.

In an embodiment of the disclosure herein, the layer or substrate contacting the amorphous layer from the other side may be the support substrate. Such a composite substrate can be manufactured by directly bonding the electro-optic crystal substrate to the surface of the support substrate. In this configuration, the first conductive layer and/or the first bonding layer may be arranged in addition to the low-refractive-index layer on the electro-optic crystal substrate.

In an embodiment of the disclosure herein, the composite substrate may further comprise a second bonding layer located between the amorphous layer and the support substrate. In this case, the layer or substrate contacting the amorphous layer from the other side may be the second bonding layer. A material constituting the second bonding layer may be, but not particularly limited to, a material suitable for direct bonding, such as tantalum oxide (Ta₂O₅), niobium oxide (Nb₂O₅), silicon (Si), aluminum oxide (Al₂O₃), and titanium oxide (TiO₂), for example.

In the aforementioned embodiment, the composite substrate may further comprise a second low-refractive-index layer located between the second bonding layer and the support substrate and having a lower refractive index than the electro-optic crystal substrate. Generally, a refractive index is proportional to a square root of a dielectric constant, thus the second low-refractive-index layer has a low dielectric constant. As such, when the composite substrate has the second low-refractive-index layer, it becomes easy to satisfy a speed matching condition and adjust a characteristic impedance in the electro-optic element manufactured from the composite substrate. Further, since stray capacitance and dielectric loss can be reduced, fast-speed operation and voltage reduction of the electro-optic element are enabled.

In the aforementioned embodiment, the composite substrate may further comprise a second conductive layer located between the second low-refractive-index layer and the support substrate. In the electro-optic element manufactured from the composite substrate, the second conductive layer may be used as an electrode for applying an electric signal (that is, an electric field) to the electro-optic crystal substrate. Alternatively, the second conductive layer may be used as a shield for suppressing the electric field from leaking from the electro-optic element.

In an embodiment of the disclosure herein, the composite substrate may further comprise a second conductive layer located between the amorphous layer and the support substrate. In this case, the layer or substrate contacting the amorphous layer from the other side may be the second conductive layer. Such a composite substrate can be manufactured by directly bonding the electro-optic crystal substrate on which the second conductive layer is deposited to the support substrate. In the electro-optic element manufactured from the composite substrate, the second conductive layer may be used as an electrode for applying an electric signal (that is, an electric field) to the electro-optic crystal substrate. Alternatively, the second conductive layer may be used as a shield for suppressing the electric field from leaking from the electro-optic element.

The second conductive layer may comprise a layer of gold (Au), silver (Ag), copper (Cu), aluminum (Al), platinum (Pt), or an alloy containing at least two of the aforementioned elements. The second conductive layer may have a single layer structure or a multiple layer structure.

A surface layer of the second conductive layer contacting the amorphous layer may be constituted of platinum. Platinum is a material suitable for direct bonding. Due to this, when the surface layer of the second conductive layer is constituted of platinum, the support substrate on which the second conductive layer is deposited can suitably be bonded directly to the electro-optic crystal substrate.

In an embodiment of the disclosure herein, the composite substrate may further comprise a second low-refractive-index layer located between the amorphous layer and the support substrate and having a lower refractive index than the electro-optic crystal substrate. In this case, the layer or substrate contacting the amorphous layer from the other side may be the second low-refractive-index layer. As aforementioned, since the refractive index is proportional to the square root of the dielectric constant, the second low-refractive-index layer has a low dielectric constant. As such, when the composite substrate has the second low-refractive-index layer, the dielectric loss is reduced in the electro-optic element manufactured from the composite substrate.

In the aforementioned embodiment, the composite substrate may further comprise a second conductive layer located between the second low-refractive-index layer and the support substrate. In the electro-optic element manufactured from the composite substrate, the second conductive layer may be used as an electrode for applying an electric signal (that is, an electric field) to the electro-optic crystal substrate. Alternatively, the second conductive layer may be used as a shield for suppressing the electric field from leaking from the electro-optic element.

In an embodiment of the disclosure herein, a ridge portion may be defined on a surface of the electro-optic crystal substrate. When the ridge portion is defined in advance on the composite substrate, the electro-optic element requiring a ridge type light waveguide can easily be manufactured. In addition to or as an alternative to the ridge portion, the electro-optic crystal substrate may comprise an optical waveguide region doped with impurities (such as titanium or zinc). The optical waveguide region doped with impurities exhibits a small increase in the refractive index due to the doped impurities, by which an optical confinement effect thereof is small, and an optical near field pattern (near field diameter) becomes relatively large. As a result, an electric field efficiency decreases in the electro-optic element manufactured from the composite substrate, and a required driving voltage becomes larger. Due to this, an element size also becomes larger. From aspects of driving voltage reduction and size reduction, a ridge type optical waveguide with a large optical confinement effect is preferable.

In the aforementioned embodiment, a c-axis (that is, a crystallographic axis) of the electro-optic crystal substrate may be parallel to the electro-optical crystal substrate. That is, the electro-optic crystal substrate may be a x-cut or y-cut substrate. In this case, the composite substrate may further comprise a first electrode located on one side surface of the ridge portion and a second electrode located on another side surface of the ridge portion and opposing the first electrode across the ridge portion. These first and second electrodes may be used as electrodes for applying an electric signal (that is, an electric field) to the ridge type optical waveguide upon manufacturing the electro-optic element from the composite substrate.

Alternatively, the c-axis (that is, the crystallographic axis) of the electro-optic crystal substrate may be perpendicular to the electro-optic crystal substrate. That is, the electro-optic crystal substrate may be a z-cut substrate. In this case, the composite substrate may further comprise a first electrode located on a top surface of the ridge portion and a second electrode located in a region within the surface of the electro-optic crystal substrate and excluding the ridge portion. These first and second electrodes may be used as electrodes for applying an electric signal (that is, an electric field) to the ridge type optical waveguide in the electro-optic element manufactured from the composite substrate.

In an embodiment in which the electro-optic crystal substrate comprises the ridge portion, an optical waveguide region containing impurities may be defined within the ridge portion along a longitudinal direction of the ridge portion. According to such a configuration, by changing a region where the impurities are to be doped, a desired optical waveguide can easily be fabricated without modifying the ridge portion.

Representative, non-limiting examples of the present disclosure will now be described in further detail with reference to the attached drawings. This detailed description is merely intended to teach a person of skill in the art further details for practicing aspects of the present teachings and is not intended to limit the scope of the present disclosure. Furthermore, each of the additional features and teachings disclosed below may be utilized separately or in conjunction with other features and teachings to provide improved composite substrates, as well as methods for using and manufacturing the same.

Moreover, combinations of features and steps disclosed in the following detailed description may not be necessary to practice the present disclosure in the broadest sense, and are instead taught merely to particularly describe representative examples of the present disclosure. Furthermore, various features of the above-described and below-described representative examples, as well as the various independent and dependent claims, may be combined in ways that are not specifically and explicitly enumerated in order to provide additional useful embodiments of the present teachings.

All features disclosed in the description and/or the claims are intended to be disclosed separately and independently from each other for the purpose of original written disclosure, as well as for the purpose of restricting the claimed subject matter, independent of the compositions of the features in the embodiments and/or the claims. In addition, all value ranges or indications of groups of entities are intended to disclose every possible intermediate value or intermediate entity for the purpose of original written disclosure, as well as for the purpose of restricting the claimed subject matter.

EMBODIMENTS

(First Embodiment) A composite substrate 10 and a method of manufacturing the same will be described with reference to the drawings. The composite substrate 10 of the present embodiment may be employed in various electro-optic elements such as an optical modulator. As shown in FIG. 1, the composite substrate 10 of the present embodiment is manufactured in a form of a so-called wafer and is supplied to a manufacturer of the electro-optic element as such. Although this is merely an example, a diameter of the composite substrate 10 is about 10 centimeters (4 inches). Normally, a plurality of electro-optic elements is manufactured from one composite substrate 10. The composite substrate 10 may not be limited to the form of a wafer, and may be manufactured in various forms and supplied as such.

As shown in FIGS. 1 and 2, the composite substrate 10 includes an electro-optic crystal substrate 12, a support substrate 14, a low-refractive-index layer 16, and an amorphous layer 18. The electro-optic crystal substrate 12 is bonded to the support substrate 14 via the low-refractive-index layer 16 and the amorphous layer 18. These substrates 12, 14 and layers 16, 18 extend parallel to each other throughout the composite substrate 10.

The electro-optic crystal substrate 12 includes a top surface 12 a exposed to outside and a bottom surface 12 b located inside the composite substrate 10. A part of or an entirety of the electro-optic crystal substrate 12 is structured as an optical waveguide configured to transmit light in an electro-optic element manufactured from the composite substrate 10. The electro-optic crystal substrate 12 is constituted of a crystal of a material having an electro-optic effect. More specifically, when an electric field is applied to the electro-optic crystal substrate 12, a refractive index of the electro-optic crystal substrate 12 thereby changes. Specially, when the electric field is applied along a c-axis of the electro-optic crystal substrate 12, the refractive index of the electro-optic crystal substrate 12 changes significantly. Here, the c-axis of the electro-optic crystal substrate 12 may be parallel to the electro-optic crystal substrate 12. That is, the electro-optic crystal substrate 12 may for example be a x-cut or y-cut substrate. Alternatively, the c-axis of the electro-optic crystal substrate 12 may be perpendicular to the electro-optic crystal substrate 12. That is, the electro-optic crystal substrate 12 may for example be a z-cut substrate. A thickness T12 of the electro-optic crystal substrate 12 may for example be, but not particularly limited to, 0.1 micrometers or more and 10 micrometers or less.

The material constituting the electro-optic crystal substrate 12 may be, but not particularly limited to, a substrate of lithium niobate (LiNbO₃: LN), lithium tantalate (LiTaO₃: LT), potassium titanyl phosphate (KTiOPO₄: KTP), potassium lithium niobate (K_(x)Li_((1-x))NbO₂: KLN), potassium niobate (KNbO₃: KN), potassium tantalate niobate (KNb_(x)Ta_((1-x))O₃: KTN), or a solid solution of lithium niobate and lithium tantalite. The electro-optic crystal substrate 12 may have an electro-optic effect of changing other optical constants, in addition to or as an alternative to the refractive index.

The support substrate 14 includes a top surface 14 a located inside the composite substrate 10 and a bottom surface 14 b exposed to outside. The electro-optic crystal substrate 12 is bonded to the support substrate 14. The support substrate 14 is provided to increase a strength of the composite substrate 10, by which the thickness of the electro-optic crystal substrate 12 can be reduced. The support substrate 14 may be, but not particularly limited to, a substrate of silicon (Si), glass, sialon (Si₃N₄—Al₂O₃), mullite (3Al₂O₃.2SiO₂, 2Al₂O₃.SiO₂), aluminum nitride (AlN), silicon nitride (Si₃N₄), magnesium oxide (MgO), sapphire, quartz, crystal, gallium nitride (GaN), silicon carbide (SiC), or gallium oxide (Ga₂O₃), for example. In order to suppress thermal deformation (especially warping) of the composite substrate 10, a linear expansion coefficient of a material constituting the support substrate 14 is preferably closer to a linear expansion coefficient of the material constituting the electro-optic crystal substrate 12. Although not particularly limited, a linear expansion coefficient of a material constituting the support substrate 24 is preferably within a range of ±50 percent of the linear expansion coefficient of the material constituting the electro-optic crystal substrate 12.

The low-refractive-index layer 16 is located between the electro-optic crystal substrate 12 and the amorphous layer 18, and is disposed along the bottom surface 12 b of the electro-optic crystal substrate 12. The low-refractive-index layer 16 has a lower refractive index than the electro-optic crystal substrate 12. Due to this, light transmitted through the electro-optic crystal substrate 12 tends to be fully reflected on the bottom surface 12 b of the electro-optic crystal substrate 12 (that is, an interface contacting the low-refractive-index layer 16), thus is suppressed from leaking from the electro-optic crystal substrate 12. The low-refractive-index layer 16 may be constituted of, but not particularly limited to, at least one selected from a group consisting of silicon oxide (SiO₂), tantalum oxide (Ta₂O₅), aluminum oxide (Al₂O₃), magnesium fluoride (MgF₂), and calcium fluoride (MgF₂), for example. A thickness T16 of the low-refractive-index layer 16 may be, but not particularly limited to, 0.1 micrometer or more and 10 micrometers or less, for example.

Generally, a refractive index is proportional to a square root of a dielectric constant. Since the refractive index of the low-refractive-index layer 16 is lower than the refractive index of the electro-optic crystal substrate 12, a dielectric constant of the low-refractive-index layer 16 is lower than a dielectric constant of the electro-optic crystal substrate 12. Thus, when the composite substrate 10 has the low-refractive-index layer 16, it becomes easy to satisfy a speed matching condition and adjust a characteristic impedance in the electro-optic elements manufactured from the composite substrate 10. Further, since stray capacitance and dielectric loss can be reduced, fast-speed operation and voltage reduction of the electro-optic element are enabled.

The amorphous layer 18 is located between the low-refractive-index layer 16 and the support substrate 14. The amorphous layer 18 has an amorphous structure, and is constituted of elements constituting the low-refractive-index layer 16 contacting the amorphous layer 18 from above and elements constituting the support substrate 14 contacting the amorphous layer 18 from below. A thickness T18 of the amorphous layer 18 may be, but not particularly limited to, 0.1 nanometer or more and 100 nanometers or less. As will be described later, the composite substrate 10 can be manufactured by directly bonding the support substrate 14 to the electro-optic crystal substrate 12 on which the low-refractive-index layer 16 is deposited. The amorphous layer 18 is a layer generated by this direct bonding, and is formed by atoms in the low-refractive-index layer 16 and the support substrate 14 diffusing. As such, a top surface 18 a of the amorphous layer 18 (that is, an interface contacting the low-refractive-index layer 16) and a bottom surface 18 b of the amorphous layer 18 (that is, an interface contacting the support substrate 14) are not necessarily flat.

Generally, an amorphous layer generated by the direct bonding is constituted of elements constituting materials located above and below the amorphous layer and does not have crystallinity, and different elements may be incorporated to the amorphous layer from outside, thus optical properties of the amorphous layer differs from those of the materials located above and below. Further, interfaces of the amorphous layer are not flat, and optical absorption and diffusion may occur. Due to this, if the amorphous layer 18 directly contacts the electro-optic crystal substrate 12, the light transmitted through the electro-optic crystal substrate 12 is attenuated by the amorphous layer 18. Contrary to this, in the composite substrate 10 of the present embodiment, the low-refractive-index layer 16 is interposed between the amorphous layer 18 and the electro-optic crystal substrate 12, and the amorphous layer 18 is not in contact with the electro-optic crystal substrate 12. As such, the light transmitted through the electro-optic crystal substrate 12 is not diffused by the amorphous layer 18 or on the top surface 18 a thereof. In addition, the low-refractive-index layer 16 contacting the electro-optic crystal substrate 12 has the lower refractive index than the electro-optic crystal substrate 12, by which it can suppress the leakage of the light transmitting through the electro-optic crystal substrate 12 and propagate the same in the optical waveguide, similar to a clad in an optical fiber.

As above, in the composite substrate 10 of the present embodiment, since the electro-optic crystal substrate 12 is strengthened by the support substrate 14, the thickness T12 of the electro-optic crystal substrate 12 can be made relatively small. Further, since an optical waveguide structure with an excellent optical confinement effect can be constructed due to the low-refractive-index layer 16, the light can be propagated in a high-quality bulk crystal with no impurities doped therein. Further, the electro-optic crystal substrate 12 and the support substrate 14 are directly bonded without using adhesive, thus are free of deterioration and deformation of the adhesive, and have high reliability. Further, dielectric loss caused by the adhesive also does not occur. Further, since the amorphous layer 18 generated by the direct bonding is separated from the electro-optic crystal substrate 12 by the low-refractive-index layer 16, the light transmitted through the electro-optic crystal substrate 12 can be propagated toward an output side without causing any loss.

Next, a method of manufacturing the composite substrate 10 will be described with reference to FIGS. 3 to 5. Firstly, as shown in FIG. 3, the electro-optic crystal substrate 12 is prepared. The electro-optic crystal substrate 12 may be an x-cut or y-cut substrate (with the c-axis being parallel to the substrate). Further, in a case where a reverse polarized portion is formed, the electro-optic crystal substrate 12 may be an offset substrate in which the c-axis and a horizontal surface of the substrate meet at an angle 10° or less. Alternatively, it may be a z-cut substrate (with the c-axis being perpendicular to the substrate). Next, as shown in FIG. 4, the low-refractive-index layer 16 is deposited on the bottom surface 12 b of the electro-optic crystal substrate 12. This deposition of the low-refractive-index layer 16 may be executed by, but not particularly limited to, vapor deposition (physical vapor deposition or chemical vapor deposition). The bottom surface 12 b of the electro-optic crystal substrate 12 is one of main surfaces of the electro-optic crystal substrate 12. Next, as shown in FIG. 5, the support substrate 14 is prepared, and the support substrate 14 is directly bonded to the bottom surface 12 b of the electro-optic crystal substrate 12 on which the low-refractive-index layer 16 is deposited. At this occasion, the aforementioned amorphous layer 18 is formed between the support substrate 14 and the low-refractive-index layer 16. Due to this, the composite substrate 10 shown in FIGS. 1 and 2 is manufactured.

In regard to the aforementioned direct bonding, specific order of processes and processing condition are not particularly limited. These may suitably be set according to respective materials of the layers or substrates to be bonded to each other. As one example, in the manufacturing method of the present embodiment, firstly, neutralization beam is irradiated to each of bonding surfaces in a high vacuum chamber (such as at about 1×10⁻⁶ Pascal). Due to this, the respective bonding surfaces are activated. Then, the activated bonding surfaces are brought into contact with each other in a high vacuum atmosphere, and are bonded at a normal temperature. A load at this bonding can be set for example to 100 to 20000 Newton. In this manufacturing method, upon executing surface activation by the neutralization beam, inert gas is introduced into the chamber and a high voltage is applied from a DC power source to an electrode disposed inside the chamber. Due to this, an electric field is generated between the electrode (positive electrode) and the chamber (negative electrode) and then electrons move, by which beam constituted of atoms and ions is generated from the inert gas. Of the beam having reached a grid, ion beam is neutralized by the grid, by which neutral atom beam is emitted from a fast atom beam source. An atomic species constituting the beam is preferably an inert gas element (such as argon (Ar), nitrogen (N), etc.). A voltage upon the activation by the beam irradiation may be set to 0.5 to 2.0 kilovolts and current thereof may be set to 50 to 200 milliamperes.

As shown in FIG. 6, in the composite substrate 10, electrodes 32, 34 for forming an electric field in the electro-optic crystal substrate 12 may be mounted on the top surface 12 a of the electro-optic crystal substrate 12. A material constituting the electrodes 32, 34 may simply need to be a conductor, and may be metal such as gold (Au), silver (Ag), copper (Cu), aluminum (Al), and platinum (Pt). The electrodes 32, 34 may each include a layer of titanium (Ti), chromium (Cr), nickel (Ni), or platinum (Pt) as a base layer (lowermost layer) contacting the electro-optic crystal substrate 12 for preventing exfoliation and migration of the electrodes 32, 34. Numbers, positions, and shapes of the electrodes 32, 34 are not particularly limited. For example, as to the numbers of the electrodes 32, 34, they may suitably be set according to the number of electro-optic elements to be manufactured from the composite substrate 10 and the numbers of the electrodes 32, 34 which each electro-optic element requires. When the electrodes 32, 34 are pre-mounted on the composite substrate 10, a manufacturer of the electro-optic elements can easily manufacture the electro-optic elements from the composite substrate 10. The electrodes 32, 34 shown in FIG. 6 may be mounted similarly to composite substrates 10 a to 10 j of other embodiments to be described later.

In addition to or alternatively, an optical waveguide region 36 may be disposed in the electro-optic crystal substrate 12 by doping impurities. In the electro-optic crystal substrate 12, the refractive index can be selectively (that is, locally) increased by doping specific impurities such as titanium or zinc, and the optical waveguide region 36 can thereby be constructed. The number, position, and shape of the optical waveguide region 36 are not particularly limited. For example, as to the number of the optical waveguide region 36, it may suitably be set according to the number of electro-optic elements to be manufactured from the composite substrate 10 and the number of the optical waveguide region 36 which each electro-optic element requires. When the optical waveguide region 36 is disposed in advance in the composite substrate 10, the manufacturer of the electro-optic elements can easily manufacture the electro-optic elements from the composite substrate 10. The optical waveguide region 36 shown in FIG. 6 may be disposed similarly in the composite substrates 10 a to 10 j of other embodiments to be described later.

As shown in FIG. 7, a ridge portion 13 may be disposed on the top surface 12 a of the electro-optic crystal substrate 12. The ridge portion 13 is a protruding portion extending in an elongate shape along the top surface 12 a. The ridge portion 13 configures a ridge type optical waveguide in the electro-optic element manufactured from the composite substrate 10. When the ridge portion 13 is disposed on the composite substrate 10 in advance, electro-optic elements requiring the ridge type optical waveguide can easily be manufactured. A width W of the ridge portion 13 may be, but not particularly limited to, 1 micrometer or more and 10 micrometer or less. A height TR of the ridge portion 13 may be, but also not particularly limited to, 10 percent or more and 95 percent or less of the thickness T12 of the electro-optic crystal substrate 12. The number, position, and shape of the ridge portion 13 are also not particularly limited. Although this is merely an example, when the composite substrate 10 is used for manufacturing a Mach-Zehnder electro-optic modulator, two ridge portions 13 at least partially extending parallel to each other are preferably disposed. The ridge portion 13 shown in FIG. 7 may be disposed similarly in the composite substrates 10 a to 10 j of other embodiments to be described later.

As shown in FIG. 8, the composite substrate 10 including the ridge portion 13 may further include a first electrode 42 and a second electrode 44. Here, in the case where the c-axis of the electro-optic crystal substrate 12 is parallel to the electro-optic crystal substrate 12, the first electrode 42 is preferably mounted on one side surface 13 a of the ridge portion 13. Further, the second electrode 44 is preferably mounted on another side surface 13 b of the ridge portion 13 to oppose the first electrode 42 across the ridge portion 13. According to such a configuration, the first electrode 42 and the second electrode 44 can apply an electric field parallel to the c-axis with respect to the ridge portion 13 that is to be the optical waveguide in the electro-optic element. A material constituting the first electrode 42 and the second electrode 44 may simply need to be a conductor, and may be metal such as gold (Au), copper (Cu), and aluminum (Al). The electrodes 42, 44 may each include a layer of titanium (Ti), chromium (Cr), nickel (Ni), or platinum (Pt) as a base layer (lowermost layer) contacting the electro-optic crystal substrate 12 for preventing exfoliation and migration of the electrodes 42, 44. Further, a low-refractive-index film having a lower refractive index than the electro-optic crystal substrate 12 may be disposed between the first electrode 42 and the electro-optic crystal substrate 12 and also between the second electrode 44 and the electro-optic crystal substrate 12. Such a low-refractive-index film functions as a clad layer, and can suppress loss in light transmitted through the ridge portion 13. Together with the ridge portion 13, the first electrode 42 and the second electrode 44 shown in FIG. 8 may be mounted similarly to the composite substrates 10 a to 10 j of other embodiments to be described later.

As shown in FIG. 9, the c-axis of the electro-optic crystal substrate 12 may be perpendicular to the electro-optic crystal substrate 12. In this case as well, the ridge portion 13 may be disposed on the top surface 12 a of the electro-optic crystal substrate 12. Further, a first electrode 52 and a second electrode 54 may be mounted on the top surface 12 a of the electro-optic crystal substrate 12. However, the first electrode 52 is preferably mounted on a top surface 13 c of the ridge portion 13 and the second electrode 54 may preferably be provided in a region within the top surface 12 a of the electro-optic crystal substrate 12 excluding the ridge portion 13. According to such a configuration, the first electrode 52 and the second electrode 54 can apply an electric field parallel to the c-axis with respect to the ridge portion 13 that is to be the optical waveguide in the electro-optic element. Together with the ridge portion 13, the first electrode 52 and the second electrode 54 shown in FIG. 9 may be mounted similarly to the composite substrates 10 a to 10 j of other embodiments to be described later. In cases where the composite substrates 10 a to 10 j are provided with conductive layers 20, 20′, the conductive layers 20, 20′ may each be used as a substitute to the second electrode 54. In these cases, the second electrode 54 may not be necessary, and thus may be omitted.

(Second Embodiment) A composite substrate 10 a of a second embodiment will be described with reference to FIGS. 10 and 11. As shown in FIG. 10, the composite substrate 10 a of the second embodiment further includes a first conductive layer 20, and thus differs from the composite substrate 10 of the first embodiment in this regard. The first conductive layer 20 is located between the low-refractive-index layer 16 and the amorphous layer 18, and contacts the amorphous layer 18 from above. As such, the amorphous layer 18 in the present embodiment is constituted of elements constituting the first conductive layer 20 and the elements constituting the support substrate 14. The first conductive layer 20 may be used as an electrode for applying an electric signal (that is, an electric field) to the electro-optic crystal substrate 12 in an electro-optic element manufactured from the composite substrate 10 a. Alternatively, the first conductive layer 20 may be used as a shield for suppressing the electric field from leaking from the electro-optic element.

A material constituting the first conductive layer 20 may simply be a conductor, and for example, it may include a layer of gold (Au), silver (Ag), copper (Cu), aluminum (Al), platinum (Pt), or an alloy containing at least two of the aforementioned elements. The first conductive layer 20 may have a single layer structure or a multiple layer structure. The first conductive layer 20 may include a layer of titanium (Ti), chromium (Cr), nickel (Ni), or platinum (Pt) as a base layer contacting the low-refractive-index layer 16 for preventing exfoliation and migration of the first conductive layer 20. A thickness T20 of the first conductive layer may be, but not particularly limited to, 0.05 micrometer or more and 5 micrometer or less.

As shown in FIG. 11, the composite substrate 10 a of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. However, in a manufacturing method of the present embodiment, the low-refractive-index layer 16 and the first conductive layer 20 are deposited on the bottom surface 12 b of the electro-optic crystal substrate 12 prior to performing the direct bonding. The low-refractive-index layer 16 is deposited on the bottom surface 12 b of the electro-optic crystal substrate 12, and the first conductive layer 20 is deposited on the low-refractive-index layer 16. As such, the direct bonding in this embodiment is performed between the first conductive layer 20 and the support substrate 14. In this case, a surface layer 20 a of the first conductive layer 20 may be constituted of platinum. Platinum is a material suitable for direct bonding. Due to this, when the surface layer 20 a of the first conductive layer 20 is constituted of platinum, the electro-optic crystal substrate 12 on which the first conductive layer 20 is deposited can suitably be bonded directly to the support substrate 14. The deposition of the first conductive layer 20 may be performed for example by sputtering or vapor deposition (physical vapor deposition or chemical vapor deposition).

(Third Embodiment) A composite substrate 10 b of a third embodiment will be described with reference to FIGS. 12 and 13. As shown in FIG. 12, the composite substrate 10 b of the third embodiment further includes a first bonding layer 22, and thus differs from the composite substrate 10 b of the second embodiment in this regard. The first bonding layer 22 is located between the first conductive layer 20 and the amorphous layer 18, and contacts the amorphous layer 18 from above. As such, the amorphous layer 18 in the present embodiment is constituted of elements constituting the first bonding layer 22 and the elements constituting the support substrate 14.

A material constituting the first bonding layer 22 preferably is, a material suitable for direct bonding, such as, but not particularly limited to, tantalum oxide (Ta₂O₅), niobium oxide (Nb₂O₅), silicon (Si), aluminum oxide (Al₂O₃), and titanium oxide (TiO₂), for example. A thickness T22 of the first bonding layer 22 may be, but not particularly limited to, 0.01 micrometer or more and 0.5 micrometer or less. Since the first bonding layer 22 is separated from the electro-optic crystal substrate 12 by the first conductive layer 20, it does not substantially affect characteristics of the composite substrate 10 b.

As shown in FIG. 13, the composite substrate 10 b of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. However, in a manufacturing method of the present embodiment, the low-refractive-index layer 16, the first conductive layer 20, and the first bonding layer 22 are deposited on the bottom surface 12 b of the electro-optic crystal substrate 12 prior to performing the direct bonding. The low-refractive-index layer 16 is deposited on the bottom surface 12 b of the electro-optic crystal substrate 12, and the first conductive layer 20 is deposited on the low-refractive-index layer 16. And, the first bonding layer 22 is deposited on the first conductive layer 20. As such, the direct bonding in this embodiment is performed between the first bonding layer 22 and the support substrate 14. Since the first bonding layer 22 is constituted of a material suitable for direct bonding, the electro-optic crystal substrate 12 on which the first bonding layer 22 is deposited can suitably be bonded directly to the support substrate 14. The deposition of the first bonding layer 22 may be performed by, but not particularly limited to, sputtering or vapor deposition (physical vapor deposition or chemical vapor deposition).

(Fourth Embodiment) A composite substrate 10 c of a fourth embodiment will be described with reference to FIGS. 14 and 15. As shown in FIG. 14, the composite substrate 10 c of the fourth embodiment further includes a second bonding layer 22′, and thus differs from the composite substrate 10 c of the third embodiment in this regard. The second bonding layer 22′ is located between the amorphous layer 18 and the support substrate 14, and contacts the amorphous layer 18 from below. As such, the amorphous layer 18 in the present embodiment is constituted of the elements constituting the first bonding layer 22 and elements constituting the second bonding layer 22′.

A material constituting the second bonding layer 22′ preferably is a material suitable for direct bonding, such as, but not particularly limited to, tantalum oxide (Ta₂O₅), niobium oxide (Nb₂O₅), silicon (Si), aluminum oxide (Al₂O₃), and titanium oxide (TiO₂), for example. A thickness T22′ of the second bonding layer 22′ may be, but not particularly limited to, 0.01 micrometer or more and 0.5 micrometer or less. Since the second bonding layer 22′ is separated from the electro-optic crystal substrate 12 by the first conductive layer 20, it does not substantially affect characteristics of the composite substrate 10 c.

As shown in FIG. 15, the composite substrate 10 c of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. However, in a manufacturing method of the present embodiment, the second bonding layer 22′ is deposited on the top surface 14 a of the support substrate 14 prior to performing the direct bonding. The low-refractive-index layer 16, the first conductive layer 20, and the first bonding layer 22 are deposited on the bottom surface 12 b of the electro-optic crystal substrate 12, similar to the third embodiment. As such, the direct bonding in this embodiment is performed between the first bonding layer 22 and the second bonding layer 22′. Since the first bonding layer 22 and the second bonding layer 22′ are constituted of material(s) suitable for direct bonding, the electro-optic crystal substrate 12 on which the first bonding layer 22 is deposited can suitably be bonded directly to the support substrate 14 on which the second bonding layer 22′ is deposited. The deposition of the second bonding layer 22′ may be performed for example by vapor deposition (physical vapor deposition or chemical vapor deposition), similar to the first bonding layer 22.

(Fifth Embodiment) A composite substrate 10 d of a fifth embodiment will be described with reference to FIGS. 16 and 17. As shown in FIG. 16, the composite substrate 10 d of the fifth embodiment does not include the first conductive layer 20, and thus differs from the composite substrate 10 b of the third embodiment in this regard. That is, the first conductive layer 20 may not be necessarily required. As shown in FIG. 17, the composite substrate 10 d of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. In a manufacturing method of the present embodiment, the low-refractive-index layer 16 and the first bonding layer 22 are deposited on the bottom surface 12 b of the electro-optic crystal substrate 12 prior to performing the direct bonding. The low-refractive-index layer 16 is deposited on the bottom surface 12 b of the electro-optic crystal substrate 12, and the first bonding layer 22 is deposited on the low-refractive-index layer 16. As such, the direct bonding in this embodiment is performed between the first bonding layer 22 and the support substrate 14.

(Sixth Embodiment) A composite substrate 10 e of a sixth embodiment will be described with reference to FIGS. 18 and 19. As shown in FIG. 18, the composite substrate 10 e of the sixth embodiment further includes the second bonding layer 22′, and thus differs from the composite substrate 10 d of the fifth embodiment in this regard. In other words, the composite substrate 10 e of the present embodiment does not include the first conductive layer 20, and thus differs from the composite substrate 10 c of the fourth embodiment in this regard. As shown in FIG. 19, the composite substrate 10 e of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. In a manufacturing method of the present embodiment, the low-refractive-index layer 16 and the first bonding layer 22 are formed on the bottom surface 12 b of the electro-optic crystal substrate 12 prior to performing the direct bonding. Further, the second bonding layer 22′ is deposited on the top surface 14 a of the support substrate 14. As such, the direct bonding in this embodiment is performed between the first bonding layer 22 and the second bonding layer 22′.

(Seventh Embodiment) A composite substrate 10 f of a seventh embodiment will be described with reference to FIGS. 20 and 21. As shown in FIG. 20, the composite substrate 10 f of the seventh embodiment further includes a second conductive layer 20′, and thus differs from the composite substrate 10 of the first embodiment in this regard. The second conductive layer 20′ is located between the amorphous layer 18 and the support substrate 14, and contacts the amorphous layer 18 from below. As such, the amorphous layer 18 in the present embodiment is constituted of elements constituting the low-refractive-index layer 16 and elements constituting the second conductive layer 20′. The second conductive layer 20′ may be used as an electrode for applying an electric signal (that is, an electric field) to the electro-optic crystal substrate 12 in an electro-optic element manufactured from the composite substrate 10 f. Alternatively, the second conductive layer 20′ may be used as a shield for suppressing the electric field from leaking from the electro-optic element.

A material constituting the second conductive layer 20′ may simply be a conductor, and for example, it may include a layer of gold (Au), silver (Ag), copper (Cu), aluminum (Al), platinum (Pt), or an alloy containing at least two of the aforementioned elements. The second conductive layer 20′ may have a single layer structure or a multiple layer structure. The second conductive layer 20′ may include a layer of titanium (Ti), chromium (Cr), nickel (Ni), or platinum (Pt) as a base layer contacting the support substrate 14 for preventing exfoliation and migration of the second conductive layer 20′. A thickness T20′ of the second conductive layer 20′ may be, but not particularly limited to, 0.05 micrometer or more and 5 micrometer or less.

As shown in FIG. 21, the composite substrate 10 f of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. However, in a manufacturing method of the present embodiment, the second conductive layer 20′ is deposited on the top surface 14 a of the support substrate 14 prior to performing the direct bonding. The low-refractive-index layer 16 is deposited on the bottom surface 12 b of the electro-optic crystal substrate 12, similar to the first embodiment. As such, the direct bonding in this embodiment is performed between the low-refractive-index layer 16 and the second conductive layer 20′. In this case, a surface layer 20 a′ of the second conductive layer 20′ may be constituted of platinum. As aforementioned, platinum is a material suitable for direct bonding. Due to this, when the surface layer 20 a′ of the second conductive layer 20′ is constituted of platinum, the electro-optic crystal substrate 12 can suitably be bonded directly to the support substrate 14 on which the second conductive layer 20′ is deposited. The deposition of the second conductive layer 20′ may be performed for example by sputtering or vapor deposition (physical vapor deposition or chemical vapor deposition).

(Eighth Embodiment) A composite substrate 10 g of an eighth embodiment will be described with reference to FIGS. 22 and 23. As shown in FIG. 22, the composite substrate 10 g of the eighth embodiment further includes a second low-refractive-index layer 16′, and thus differs from the composite substrate 10 f of the seventh embodiment in this regard. The second low-refractive-index layer 16′ has a lower refractive index than the electro-optic crystal substrate 12, similar to the low-refractive-index layer 16. The second low-refractive-index layer 16′ is located between the amorphous layer 18 and the support substrate 14, and contacts the amorphous layer 18 from below. As such, the amorphous layer 18 in the present embodiment is constituted of elements constituting low-refractive-index layer 16 and elements constituting the second low-refractive-index layer 16′. A thickness T16′ of the second low-refractive-index layer 16′ may be, but not particularly limited to, 0.1 micrometer or more and 10 micrometer or less, for example.

Although not particularly limited, the second low-refractive-index layer 16′ may be constituted of at least one selected from the group consisting of silicon oxide (SiO₂), tantalum oxide (Ta₂O₅), aluminum oxide (Al₂O₃), magnesium fluoride (MgF₂), and calcium fluoride (MgF₂). A material constituting the second low-refractive-index layer 16′ may be the material constituting the low-refractive-index layer 16. Alternatively, the material constituting the second low-refractive-index layer 16′ may be different from the material constituting the low-refractive-index layer 16. As aforementioned, a refractive index is proportional to a square of the dielectric constant. Since a refractive index of the second low-refractive-index layer 16′ is lower than the refractive index of the electro-optic crystal substrate 12, a dielectric constant of the second low-refractive-index layer 16′ is lower than the dielectric constant of the electro-optic crystal substrate 12. Thus, when the composite substrate 10 has the second low-refractive-index layer 16′, it becomes easy to satisfy the speed matching condition and adjust the characteristic impedance in the electro-optic elements manufactured from the composite substrate 10. Further, since the stray capacitance and dielectric loss can be reduced, the fast-speed operation and voltage reduction of the electro-optic element are enabled.

As shown in FIG. 23, the composite substrate 10 g of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. In a manufacturing method of the present embodiment, the second conductive layer 20′ and the second low-refractive-index layer 16′ are formed on the top surface 14 a of the support substrate 14 prior to performing the direct bonding. The second conductive layer 20′ is deposited on the top surface 14 a of the support substrate 14, and the second low-refractive-index layer 16′ is deposited on the second conductive layer 20′. The low-refractive-index layer 16 is deposited on the bottom surface 12 b of the electro-optic crystal substrate 12, similar to the first embodiment. As such, the direct bonding in this embodiment is performed between the low-refractive-index layer 16 and the second low-refractive-index layer 16′. The deposition of the second low-refractive-index layer 16′ may be performed by sputtering or vapor deposition (physical vapor deposition or chemical vapor deposition), similar to the low-refractive-index layer 16.

(Ninth Embodiment) A composite substrate 10 h of a ninth embodiment will be described with reference to FIGS. 24 and 25. As shown in FIG. 24, the composite substrate 10 h of the ninth embodiment further includes the first bonding layer 22 and the second bonding layer 22′, and thus differs from the composite substrate 10 g of the eighth embodiment in this regard. The first bonding layer 22 is located between the low-refractive-index layer 16 and the amorphous layer 18, and contacts the amorphous layer 18 from above. The second bonding layer 22′ is located between the amorphous layer 18 and the second low-refractive-index layer 16′, and contacts the amorphous layer 18 from below. As such, the amorphous layer 18 in the present embodiment is constituted of elements constituting the first bonding layer 22 and elements constituting the second bonding layer 22′.

As aforementioned, the first bonding layer 22 and the second bonding layer 22′ can each be constituted of the material suitable for direct bonding, such as tantalum oxide (Ta₂O₅), niobium oxide (Nb₂O₅), silicon (Si), aluminum oxide (Al₂O₃), and titanium oxide (TiO₂), for example. The first bonding layer 22 and the second bonding layer 22′ may be constituted of the same material, or may be constituted of different materials. Thicknesses T22, T22′ of the first bonding layer 22 and the second bonding layer 22′ may each be, but not particularly limited to, 0.01 micrometer or more and 0.5 micrometer or less. The thicknesses T22, T22′ of the first bonding layer 22 and the second bonding layer 22′ may be the same or different.

As shown in FIG. 25, the composite substrate 10 h of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. In a manufacturing method of the present embodiment, the low-refractive-index layer 16 and the first bonding layer 22 are formed on the bottom surface 12 b of the electro-optic crystal substrate 12 prior to performing the direct bonding. The low-refractive-index layer 16 is deposited on the bottom surface 12 b of the electro-optic crystal substrate 12, and the first bonding layer 22 is deposited on the low-refractive-index layer 16. The second conductive layer 20′, the second low-refractive-index layer 16′, and the second bonding layer 22′ are formed on the top surface 14 a of the support substrate 14. The second conductive layer 20′ is deposited on the top surface 14 a of the support substrate 14, and the second low-refractive-index layer 16′ is deposited on the second conductive layer 20′. Then, the second bonding layer 22′ is deposited on the second low-refractive-index layer 16′. As such, the direct bonding in this embodiment is performed between the first bonding layer 22 and the second bonding layer 22′. The deposition of the first bonding layer 22 and the second bonding layer 22′ may be performed by sputtering or vapor deposition (physical vapor deposition or chemical vapor deposition).

(Tenth Embodiment) A composite substrate 10 i of a tenth embodiment will be described with reference to FIGS. 26 and 27. As shown in FIG. 26, the composite substrate 10 i of the tenth embodiment does not include the second conductive layer 20′, and thus differs from the composite substrate 10 h of the ninth embodiment in this regard. That is, the second conductive layer 20′ may not be necessarily required. As shown in FIG. 27, the composite substrate 10 i of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. In a manufacturing method of the present embodiment, the low-refractive-index layer 16 and the first bonding layer 22 are formed on the bottom surface 12 b of the electro-optic crystal substrate 12 prior to performing the direct bonding. The low-refractive-index layer 16 is deposited on the bottom surface 12 b of the electro-optic crystal substrate 12 and the first bonding layer 22 is deposited on the low-refractive-index layer 16. The second low-refractive-index layer 16′ and the second bonding layer 22′ are formed on the top surface 14 a of the support substrate 14. The second low-refractive-index layer 16′ is deposited on the top surface 14 a of the support substrate 14, and the second bonding layer 22′ is deposited on the second low-refractive-index layer 16′. As such, the direct bonding in this embodiment is performed between the first bonding layer 22 and the second bonding layer 22′.

(Eleventh Embodiment) A composite substrate 10 j of an eleventh embodiment will be described with reference to FIGS. 28 and 29. As shown in FIG. 28, the composite substrate 10 j of the eleventh embodiment does not include the first bonding layer 22 and the second bonding layer 22′, and thus differs from the composite substrate 10 i of the tenth embodiment in this regard. That is, the first bonding layer 22 and the second bonding layer 22′ may not be necessarily required. As shown in FIG. 29, the composite substrate 10 j of the present embodiment can also be manufactured by directly bonding the electro-optic crystal substrate 12 to the support substrate 14. In a manufacturing method of the present embodiment, the low-refractive-index layer 16 is deposited on the bottom surface 12 b of the electro-optic crystal substrate 12, and the second low-refractive-index layer 16′ is deposited on the top surface 14 a of the support substrate 14 prior to performing the direct bonding. As such, the direct bonding in this embodiment is performed between the low-refractive-index layer 16 and the second low-refractive-index layer 16′.

REFERENCE LIST

-   10: Composite Substrate -   12: Electro-Optic Crystal Substrate -   13: Ridge Portion -   14: Support Substrate -   16: Low-Refractive-Index Layer -   16′ second Low-Refractive-Index Layer -   18: Amorphous Layer -   20: First Conductive Layer -   20′: Second Conductive Layer -   22: First Bonding Layer -   22′: Second Bonding Layer 

1. A composite substrate for an electro-optic element, the composite substrate comprising: an electro-optic crystal substrate having an electro-optic effect; a support substrate bonded to the electro-optic crystal substrate at least via an amorphous layer; a low-refractive-index layer located between the electro-optic crystal substrate and the amorphous layer, contacting the electro-optic crystal substrate, and having a lower refractive index than the electro-optical crystal substrate; and a first conductive layer located between the low-refractive-index layer and the amorphous layer, wherein the amorphous layer is constituted of one or more elements that constitute a layer or a substrate contacting the amorphous layer from one side and one or more elements that constitute a layer or a substrate contacting the amorphous layer from another side, the layer or substrate contacting the amorphous layer from the one side is the first conductive layer, and the first conductive layer comprises a layer of gold, silver, copper, aluminum, platinum, or an alloy containing at least two of the aforementioned elements.
 2. The composite substrate according to claim 1, wherein the low-refractive-index layer is constituted of at least one selected from the group consisting of silicon oxide, tantalum oxide, aluminum oxide, magnesium fluoride, and calcium fluoride.
 3. The composite substrate according to claim 1, wherein the support substrate is a substrate of sialon, mullite, silicon nitride, magnesium oxide, gallium nitride, or gallium oxide.
 4. (canceled)
 5. (canceled)
 6. (canceled)
 7. The composite substrate according to claim 1, wherein a surface layer of the first conductive layer contacting the amorphous layer is constituted of platinum.
 8. The composite substrate according to claim 1, wherein the first conductive layer contacts the low-refractive-index layer and comprises a layer of titanium, chromium, nickel, or platinum as a base layer contacting the low-refractive-index layer.
 9. (canceled)
 10. (canceled)
 11. The composite substrate according to claim 1, wherein the layer or substrate contacting the amorphous layer from the other side is the support substrate.
 12. The composite substrate according to claim 1, further comprising a second bonding layer located between the amorphous layer and the support substrate, wherein the layer or substrate contacting the amorphous layer from the other side is the second bonding layer.
 13. The composite substrate according to claim 12, wherein the second bonding layer is constituted of at least one selected from the group consisting of tantalum oxide, niobium oxide, silicon, aluminum oxide, and titanium oxide.
 14. The composite substrate according to claim 12, further comprising a second low-refractive-index layer located between the second bonding layer and the support substrate and having a lower refractive index than the electro-optic crystal substrate.
 15. (canceled)
 16. (canceled)
 17. (canceled)
 18. (canceled)
 19. The composite substrate according to claim 1, further comprising a second low-refractive-index layer located between the amorphous layer and the support substrate and having a lower refractive index than the electro-optic crystal substrate, wherein the layer or substrate contacting the amorphous layer from the other side is the second low-refractive-index layer.
 20. (canceled)
 21. The composite substrate according to claim 1, wherein a ridge portion is defined on a surface of the electro-optic crystal substrate.
 22. The composite substrate according to claim 21, wherein a c-axis of the electro-optic crystal substrate is parallel to the electro-optical crystal substrate, and the composite substrate further comprises a first electrode located on one side surface of the ridge portion and a second electrode located on another side surface of the ridge portion and opposing the first electrode across the ridge portion.
 23. The composite substrate according to claim 21, wherein a c-axis of the electro-optic crystal substrate is perpendicular to the electro-optic crystal substrate, and the composite substrate further comprises a first electrode located on a top surface of the ridge portion and a second electrode located in a region within the surface of the electro-optic crystal substrate and excluding the ridge portion.
 24. The composite substrate according to claim 21, wherein an optical waveguide region containing impurities is defined within the ridge portion along a longitudinal direction of the ridge portion.
 25. A method of manufacturing a composite substrate for an electro-optic element, the method comprising: depositing at least one layer comprising a low-refractive-index layer and a first conductive layer on an electro-optic crystal substrate having an electro-optic effect such that the low-refractive-index layer contacts the electro-optic crystal substrate, the low-refractive-index layer having a lower refractive index than the electro-optic crystal substrate; and directly bonding the at least one layer deposited on the electro-optic crystal substrate to a surface of a support substrate, wherein the first conductive layer comprises a layer of gold, silver, copper, aluminum, platinum, or an alloy containing at least two of the aforementioned elements.
 26. The method according to claim 25, wherein directly bonding of the at least one layer to the surface of the support substrate is performed in a high vacuum chamber at a normal temperature.
 27. The method according to claim 26, wherein directly bonding of the at least one layer to the surface of the support substrate comprises irradiating a neutralization beam to each bonding surface.
 28. The method according to claim 27, wherein directly bonding of the at least one layer to the surface of the support substrate is performed with a load of 100 to 20000 Newtons for a 4-inch-diameter area.
 29. A composite substrate for an electro-optic element, the composite substrate comprising: an electro-optic crystal substrate having an electro-optic effect; a support substrate bonded to the electro-optic crystal substrate at least via an amorphous layer; a low-refractive-index layer located between the electro-optic crystal substrate and the amorphous layer, contacting the electro-optic crystal substrate, and having a lower refractive index than the electro-optical crystal substrate; a first conductive layer located between the low-refractive-index layer and the amorphous layer; and a first bonding layer located between the low-refractive-index layer and the amorphous layer, wherein the amorphous layer is constituted of one or more elements that constitute a layer or a substrate contacting the amorphous layer from one side and one or more elements that constitute a layer or a substrate contacting the amorphous layer from another side, the layer or substrate contacting the amorphous layer from the one side is the first bonding layer, and the first conductive layer comprises a layer of gold, silver, copper, aluminum, platinum, or an alloy containing at least two of the aforementioned elements.
 30. The composite substrate according to claim 29, wherein the first bonding layer is constituted of at least one selected from the group consisting of tantalum oxide, niobium oxide, silicon, aluminum oxide, and titanium oxide. 